SAE-AISI 1043 Steel vs. C46200 Brass
SAE-AISI 1043 steel belongs to the iron alloys classification, while C46200 brass belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1043 steel and the bottom bar is C46200 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Elongation at Break, % | 13 to 18 | |
| 17 to 34 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 73 | |
| 40 |
| Shear Strength, MPa | 400 to 430 | |
| 240 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 650 to 710 | |
| 370 to 480 |
| Tensile Strength: Yield (Proof), MPa | 350 to 600 | |
| 120 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 120 |
| Melting Completion (Liquidus), °C | 1460 | |
| 840 |
| Melting Onset (Solidus), °C | 1420 | |
| 800 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 24 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 18 | |
| 46 |
| Embodied Water, L/kg | 46 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 87 to 100 | |
| 69 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 320 to 980 | |
| 72 to 400 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 23 to 25 | |
| 13 to 16 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 14 | |
| 35 |
| Thermal Shock Resistance, points | 21 to 22 | |
| 12 to 16 |
Alloy Composition
| Carbon (C), % | 0.4 to 0.47 | |
| 0 |
| Copper (Cu), % | 0 | |
| 62 to 65 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.0 |
| Zinc (Zn), % | 0 | |
| 33.3 to 37.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |