SAE-AISI 1050 Steel vs. EN 1.6773 Steel

Both SAE-AISI 1050 steel and EN 1.6773 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1050 steel and the bottom bar is EN 1.6773 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 220
340
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
11
Fatigue Strength, MPa 260 to 400
560
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 430 to 470
670
Tensile Strength: Ultimate (UTS), MPa 690 to 790
1120
Tensile Strength: Yield (Proof), MPa 390 to 650
910

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
450
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
46
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 18
26
Embodied Water, L/kg 46
61

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 81 to 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 400 to 1130
2210
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
40
Strength to Weight: Bending, points 22 to 24
30
Thermal Diffusivity, mm2/s 14
12
Thermal Shock Resistance, points 22 to 25
33

Alloy Composition

Carbon (C), % 0.48 to 0.55
0.32 to 0.39
Chromium (Cr), % 0
1.6 to 2.0
Iron (Fe), % 98.5 to 98.9
92 to 93.9
Manganese (Mn), % 0.6 to 0.9
0.3 to 0.6
Molybdenum (Mo), % 0
0.25 to 0.45
Nickel (Ni), % 0
3.6 to 4.1
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0 to 0.4
Sulfur (S), % 0 to 0.050
0 to 0.025