Both SAE-AISI 1055 steel and ASTM A369 grade FPA are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1055 steel and the bottom bar is ASTM A369 grade FPA.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
110
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 14
27
Fatigue Strength, MPa 260 to 390
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 440 to 450
240
Tensile Strength: Ultimate (UTS), MPa 730 to 750
380
Tensile Strength: Yield (Proof), MPa 400 to 630
240

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 12
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80 to 85
89
Resilience: Unit (Modulus of Resilience), kJ/m3 440 to 1070
150
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26
13
Strength to Weight: Bending, points 23
15
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 23 to 24
12

Alloy Composition

Carbon (C), % 0.5 to 0.6
0 to 0.25
Iron (Fe), % 98.4 to 98.9
98.3 to 99.63
Manganese (Mn), % 0.6 to 0.9
0.27 to 0.93
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0
0.1 to 0.5
Sulfur (S), % 0 to 0.050
0 to 0.035