SAE-AISI 1060 Steel vs. AWS E430

Both SAE-AISI 1060 steel and AWS E430 are iron alloys. They have 82% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1060 steel and the bottom bar is AWS E430.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 10 to 13
23
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Tensile Strength: Ultimate (UTS), MPa 620 to 740
500

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
25
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.6
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 11
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
9.0
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.2
Embodied Energy, MJ/kg 19
31
Embodied Water, L/kg 46
120

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22 to 26
18
Strength to Weight: Bending, points 21 to 23
18
Thermal Diffusivity, mm2/s 14
6.7
Thermal Shock Resistance, points 20 to 24
13

Alloy Composition

Carbon (C), % 0.55 to 0.65
0 to 0.1
Chromium (Cr), % 0
15 to 18
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 98.4 to 98.9
77.8 to 85
Manganese (Mn), % 0.6 to 0.9
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0
0 to 0.6
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0
0 to 0.9
Sulfur (S), % 0 to 0.050
0 to 0.030