SAE-AISI 1060 Steel vs. Commercially Pure Zirconium
SAE-AISI 1060 steel belongs to the iron alloys classification, while commercially pure zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1060 steel and the bottom bar is commercially pure zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 10 to 13 | |
| 18 |
| Fatigue Strength, MPa | 260 to 340 | |
| 60 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 740 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 400 to 540 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 51 | |
| 22 |
| Thermal Expansion, µm/m-K | 12 | |
| 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.7 |
| Embodied Water, L/kg | 46 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 58 to 82 | |
| 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 to 790 | |
| 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 22 to 26 | |
| 18 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 20 to 24 | |
| 56 |
Alloy Composition
| Carbon (C), % | 0.55 to 0.65 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 94.7 to 100 |