SAE-AISI 1060 Steel vs. EN 1.1061 Steel
Both SAE-AISI 1060 steel and EN 1.1061 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1060 steel and the bottom bar is EN 1.1061 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 220 | |
| 150 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 740 | |
| 530 to 1810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.6 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 26 | |
| 19 to 64 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 19 to 42 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 20 to 24 | |
| 17 to 58 |
Alloy Composition
| Carbon (C), % | 0.55 to 0.65 | |
| 0.42 to 0.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 98.1 to 99.06 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.5 to 0.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.050 | |
| 0.020 to 0.035 |