SAE-AISI 1060 Steel vs. SAE-AISI 81B45 Steel
Both SAE-AISI 1060 steel and SAE-AISI 81B45 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1060 steel and the bottom bar is SAE-AISI 81B45 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 220 | |
| 160 to 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 10 to 13 | |
| 12 to 24 |
| Fatigue Strength, MPa | 260 to 340 | |
| 250 to 350 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 370 to 450 | |
| 340 to 400 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 740 | |
| 540 to 670 |
| Tensile Strength: Yield (Proof), MPa | 400 to 540 | |
| 350 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 40 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.6 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 2.3 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 19 | |
| 20 |
| Embodied Water, L/kg | 46 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 58 to 82 | |
| 77 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 to 790 | |
| 320 to 840 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 26 | |
| 19 to 24 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 19 to 22 |
| Thermal Diffusivity, mm2/s | 14 | |
| 11 |
| Thermal Shock Resistance, points | 20 to 24 | |
| 17 to 21 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00050 to 0.0030 |
| Carbon (C), % | 0.55 to 0.65 | |
| 0.43 to 0.48 |
| Chromium (Cr), % | 0 | |
| 0.35 to 0.55 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 97 to 98 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.75 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.080 to 0.15 |
| Nickel (Ni), % | 0 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.040 |