SAE-AISI 1064 Steel vs. C87800 Brass
SAE-AISI 1064 steel belongs to the iron alloys classification, while C87800 brass belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1064 steel and the bottom bar is C87800 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 12 to 13 | |
| 25 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 72 | |
| 42 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 730 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 470 to 480 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 920 |
| Melting Onset (Solidus), °C | 1420 | |
| 820 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 410 |
| Thermal Conductivity, W/m-K | 51 | |
| 28 |
| Thermal Expansion, µm/m-K | 11 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 6.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 7.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 27 |
| Density, g/cm3 | 7.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 19 | |
| 44 |
| Embodied Water, L/kg | 46 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 79 to 81 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 600 to 630 | |
| 540 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 25 to 26 | |
| 20 |
| Strength to Weight: Bending, points | 23 | |
| 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 8.3 |
| Thermal Shock Resistance, points | 25 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.15 |
| Antimony (Sb), % | 0 | |
| 0 to 0.050 |
| Arsenic (As), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.6 to 0.7 | |
| 0 |
| Copper (Cu), % | 0 | |
| 80 to 84.2 |
| Iron (Fe), % | 98.4 to 98.9 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 to 0.15 |
| Nickel (Ni), % | 0 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 3.8 to 4.2 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.050 |
| Tin (Sn), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 12 to 16 |
| Residuals, % | 0 | |
| 0 to 0.5 |