SAE-AISI 1065 Steel vs. EN AC-51500 Aluminum
SAE-AISI 1065 steel belongs to the iron alloys classification, while EN AC-51500 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is SAE-AISI 1065 steel and the bottom bar is EN AC-51500 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 230 | |
| 80 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 68 |
| Elongation at Break, % | 11 to 14 | |
| 5.6 |
| Fatigue Strength, MPa | 270 to 340 | |
| 120 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 72 | |
| 26 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 780 | |
| 280 |
| Tensile Strength: Yield (Proof), MPa | 430 to 550 | |
| 160 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 430 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 630 |
| Melting Onset (Solidus), °C | 1420 | |
| 590 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 910 |
| Thermal Conductivity, W/m-K | 51 | |
| 120 |
| Thermal Expansion, µm/m-K | 11 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 11 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 88 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 9.5 |
| Density, g/cm3 | 7.8 | |
| 2.6 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 9.0 |
| Embodied Energy, MJ/kg | 19 | |
| 150 |
| Embodied Water, L/kg | 46 | |
| 1150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 74 to 90 | |
| 13 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 490 to 820 | |
| 190 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 52 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 29 |
| Strength to Weight: Bending, points | 23 to 24 | |
| 36 |
| Thermal Diffusivity, mm2/s | 14 | |
| 49 |
| Thermal Shock Resistance, points | 25 to 27 | |
| 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 89.8 to 93.1 |
| Carbon (C), % | 0.6 to 0.7 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Iron (Fe), % | 98.3 to 98.8 | |
| 0 to 0.25 |
| Magnesium (Mg), % | 0 | |
| 4.7 to 6.0 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0.4 to 0.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 | |
| 1.8 to 2.6 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.25 |
| Zinc (Zn), % | 0 | |
| 0 to 0.070 |
| Residuals, % | 0 | |
| 0 to 0.15 |