SAE-AISI 1074 Steel vs. Commercially Pure Zirconium
SAE-AISI 1074 steel belongs to the iron alloys classification, while commercially pure zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1074 steel and the bottom bar is commercially pure zirconium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 11 to 14 | |
| 18 |
| Fatigue Strength, MPa | 290 to 350 | |
| 60 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 36 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 820 | |
| 430 |
| Tensile Strength: Yield (Proof), MPa | 450 to 570 | |
| 240 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 50 | |
| 22 |
| Thermal Expansion, µm/m-K | 12 | |
| 5.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.7 |
| Embodied Water, L/kg | 46 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 77 to 94 | |
| 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 550 to 860 | |
| 290 |
| Stiffness to Weight: Axial, points | 13 | |
| 8.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 26 to 29 | |
| 18 |
| Strength to Weight: Bending, points | 23 to 25 | |
| 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 24 to 26 | |
| 56 |
Alloy Composition
| Carbon (C), % | 0.7 to 0.8 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Hafnium (Hf), % | 0 | |
| 0 to 4.5 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0050 |
| Iron (Fe), % | 98.3 to 98.8 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 94.7 to 100 |