SAE-AISI 1074 Steel vs. C82400 Copper

SAE-AISI 1074 steel belongs to the iron alloys classification, while C82400 copper belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1074 steel and the bottom bar is C82400 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 11 to 14
1.0 to 20
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
45
Tensile Strength: Ultimate (UTS), MPa 740 to 820
500 to 1030
Tensile Strength: Yield (Proof), MPa 450 to 570
260 to 970

Thermal Properties

Latent Heat of Fusion, J/g 250
230
Maximum Temperature: Mechanical, °C 400
270
Melting Completion (Liquidus), °C 1460
1000
Melting Onset (Solidus), °C 1420
900
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 50
130
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
25
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
26

Otherwise Unclassified Properties

Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.4
8.9
Embodied Energy, MJ/kg 19
140
Embodied Water, L/kg 46
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 77 to 94
10 to 83
Resilience: Unit (Modulus of Resilience), kJ/m3 550 to 860
270 to 3870
Stiffness to Weight: Axial, points 13
7.6
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 26 to 29
16 to 33
Strength to Weight: Bending, points 23 to 25
16 to 26
Thermal Diffusivity, mm2/s 14
39
Thermal Shock Resistance, points 24 to 26
17 to 36

Alloy Composition

Aluminum (Al), % 0
0 to 0.15
Beryllium (Be), % 0
1.6 to 1.9
Carbon (C), % 0.7 to 0.8
0
Chromium (Cr), % 0
0 to 0.1
Cobalt (Co), % 0
0.2 to 0.65
Copper (Cu), % 0
96 to 98.2
Iron (Fe), % 98.3 to 98.8
0 to 0.2
Lead (Pb), % 0
0 to 0.020
Manganese (Mn), % 0.5 to 0.8
0
Nickel (Ni), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.040
0
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0
0 to 0.1
Titanium (Ti), % 0
0 to 0.12
Zinc (Zn), % 0
0 to 0.1
Residuals, % 0
0 to 0.5