SAE-AISI 1080 Steel vs. EN 1.1192 Steel

Both SAE-AISI 1080 steel and EN 1.1192 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1080 steel and the bottom bar is EN 1.1192 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 260
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
72
Tensile Strength: Ultimate (UTS), MPa 770 to 870
520 to 1810

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 11
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 46
46

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 27 to 31
18 to 64
Strength to Weight: Bending, points 24 to 26
18 to 42
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 25 to 29
16 to 58

Alloy Composition

Carbon (C), % 0.75 to 0.88
0.42 to 0.5
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 98.1 to 98.7
98.1 to 99.08
Manganese (Mn), % 0.6 to 0.9
0.5 to 0.8
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0
0 to 0.3
Sulfur (S), % 0 to 0.050
0 to 0.025

Comparable Variants