SAE-AISI 1080 Steel vs. C17200 Copper
SAE-AISI 1080 steel belongs to the iron alloys classification, while C17200 copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1080 steel and the bottom bar is C17200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 11 | |
| 1.1 to 37 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 72 | |
| 45 |
| Shear Strength, MPa | 460 to 520 | |
| 330 to 780 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 870 | |
| 480 to 1380 |
| Tensile Strength: Yield (Proof), MPa | 480 to 590 | |
| 160 to 1250 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 230 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 280 |
| Melting Completion (Liquidus), °C | 1450 | |
| 980 |
| Melting Onset (Solidus), °C | 1410 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.6 | |
| 22 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 11 | |
| 23 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 9.4 |
| Embodied Energy, MJ/kg | 19 | |
| 150 |
| Embodied Water, L/kg | 46 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 80 to 84 | |
| 4.2 to 500 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 610 to 920 | |
| 110 to 5720 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 27 to 31 | |
| 15 to 44 |
| Strength to Weight: Bending, points | 24 to 26 | |
| 16 to 31 |
| Thermal Diffusivity, mm2/s | 14 | |
| 31 |
| Thermal Shock Resistance, points | 25 to 29 | |
| 16 to 46 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Beryllium (Be), % | 0 | |
| 1.8 to 2.0 |
| Carbon (C), % | 0.75 to 0.88 | |
| 0 |
| Copper (Cu), % | 0 | |
| 96.1 to 98 |
| Iron (Fe), % | 98.1 to 98.7 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.2 to 0.6 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |