SAE-AISI 1080 Steel vs. C41300 Brass

SAE-AISI 1080 steel belongs to the iron alloys classification, while C41300 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1080 steel and the bottom bar is C41300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11
2.0 to 44
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
42
Shear Strength, MPa 460 to 520
230 to 370
Tensile Strength: Ultimate (UTS), MPa 770 to 870
300 to 630
Tensile Strength: Yield (Proof), MPa 480 to 590
120 to 570

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 400
180
Melting Completion (Liquidus), °C 1450
1040
Melting Onset (Solidus), °C 1410
1010
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 51
130
Thermal Expansion, µm/m-K 12
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.6
30
Electrical Conductivity: Equal Weight (Specific), % IACS 11
31

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
29
Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 1.4
2.7
Embodied Energy, MJ/kg 19
44
Embodied Water, L/kg 46
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80 to 84
11 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 610 to 920
69 to 1440
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 27 to 31
9.6 to 20
Strength to Weight: Bending, points 24 to 26
11 to 19
Thermal Diffusivity, mm2/s 14
40
Thermal Shock Resistance, points 25 to 29
11 to 22

Alloy Composition

Carbon (C), % 0.75 to 0.88
0
Copper (Cu), % 0
89 to 93
Iron (Fe), % 98.1 to 98.7
0 to 0.050
Lead (Pb), % 0
0 to 0.1
Manganese (Mn), % 0.6 to 0.9
0
Phosphorus (P), % 0 to 0.040
0
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0
0.7 to 1.3
Zinc (Zn), % 0
5.1 to 10.3
Residuals, % 0
0 to 0.5