SAE-AISI 1086 Steel vs. ASTM A514 Steel

Both SAE-AISI 1086 steel and ASTM A514 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1086 steel and the bottom bar is ASTM A514 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 260
240 to 250
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11
18 to 21
Fatigue Strength, MPa 300 to 360
470 to 540
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Shear Strength, MPa 450 to 520
490 to 520
Tensile Strength: Ultimate (UTS), MPa 760 to 870
790 to 830
Tensile Strength: Yield (Proof), MPa 480 to 580
690 to 770

Thermal Properties

Latent Heat of Fusion, J/g 240
250 to 260
Maximum Temperature: Mechanical, °C 400
400 to 440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
37 to 51
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.2 to 7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.3 to 8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.3 to 3.8
Density, g/cm3 7.8
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 1.4
1.6 to 1.8
Embodied Energy, MJ/kg 19
21 to 25
Embodied Water, L/kg 45
48 to 57

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79 to 84
140 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 610 to 890
1280 to 1590
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 27 to 31
28 to 29
Strength to Weight: Bending, points 24 to 26
24 to 25
Thermal Diffusivity, mm2/s 14
10 to 14
Thermal Shock Resistance, points 26 to 30
23 to 24