SAE-AISI 1108 Steel vs. ASTM A372 Grade J Steel
Both SAE-AISI 1108 steel and ASTM A372 grade J steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1108 steel and the bottom bar is ASTM A372 grade J steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 140 | |
| 200 to 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 23 to 34 | |
| 17 to 22 |
| Fatigue Strength, MPa | 170 to 260 | |
| 310 to 570 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 250 to 280 | |
| 410 to 630 |
| Tensile Strength: Ultimate (UTS), MPa | 380 to 440 | |
| 650 to 1020 |
| Tensile Strength: Yield (Proof), MPa | 220 to 360 | |
| 430 to 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 44 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 2.4 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 18 | |
| 20 |
| Embodied Water, L/kg | 46 | |
| 51 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 to 110 | |
| 130 to 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 340 | |
| 500 to 1930 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 16 | |
| 23 to 36 |
| Strength to Weight: Bending, points | 15 to 16 | |
| 21 to 29 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 12 to 14 | |
| 19 to 30 |
Alloy Composition
| Carbon (C), % | 0.080 to 0.13 | |
| 0.35 to 0.5 |
| Chromium (Cr), % | 0 | |
| 0.8 to 1.2 |
| Iron (Fe), % | 98.9 to 99.24 | |
| 96.7 to 97.8 |
| Manganese (Mn), % | 0.6 to 0.8 | |
| 0.75 to 1.1 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 to 0.010 |