SAE-AISI 1108 Steel vs. EN 1.0562 Steel

Both SAE-AISI 1108 steel and EN 1.0562 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1108 steel and the bottom bar is EN 1.0562 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 140
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23 to 34
24
Fatigue Strength, MPa 170 to 260
270
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 250 to 280
350
Tensile Strength: Ultimate (UTS), MPa 380 to 440
550
Tensile Strength: Yield (Proof), MPa 220 to 360
370

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
50
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.3
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.6
Embodied Energy, MJ/kg 18
22
Embodied Water, L/kg 46
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95 to 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 130 to 340
360
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13 to 16
19
Strength to Weight: Bending, points 15 to 16
19
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 12 to 14
17

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0.080 to 0.13
0 to 0.18
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 98.9 to 99.24
96.2 to 98.9
Manganese (Mn), % 0.6 to 0.8
1.1 to 1.7
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0.080 to 0.13
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.1