SAE-AISI 1117 Steel vs. N06060 Nickel
SAE-AISI 1117 steel belongs to the iron alloys classification, while N06060 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1117 steel and the bottom bar is N06060 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
210 |
Elongation at Break, % | 17 to 26 | |
45 |
Fatigue Strength, MPa | 190 to 300 | |
230 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
82 |
Shear Strength, MPa | 320 to 330 | |
490 |
Tensile Strength: Ultimate (UTS), MPa | 490 to 540 | |
700 |
Tensile Strength: Yield (Proof), MPa | 260 to 460 | |
270 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
320 |
Maximum Temperature: Mechanical, °C | 400 | |
980 |
Melting Completion (Liquidus), °C | 1460 | |
1510 |
Melting Onset (Solidus), °C | 1420 | |
1450 |
Specific Heat Capacity, J/kg-K | 470 | |
430 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
65 |
Density, g/cm3 | 7.8 | |
8.7 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
12 |
Embodied Energy, MJ/kg | 18 | |
160 |
Embodied Water, L/kg | 47 | |
280 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 110 | |
250 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 550 | |
180 |
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
23 |
Strength to Weight: Axial, points | 17 to 19 | |
22 |
Strength to Weight: Bending, points | 18 to 19 | |
20 |
Thermal Shock Resistance, points | 15 to 17 | |
19 |
Alloy Composition
Carbon (C), % | 0.14 to 0.2 | |
0 to 0.030 |
Chromium (Cr), % | 0 | |
19 to 22 |
Copper (Cu), % | 0 | |
0.25 to 1.3 |
Iron (Fe), % | 98.3 to 98.8 | |
0 to 14 |
Manganese (Mn), % | 1.0 to 1.3 | |
0 to 1.5 |
Molybdenum (Mo), % | 0 | |
12 to 14 |
Nickel (Ni), % | 0 | |
54 to 60 |
Niobium (Nb), % | 0 | |
0.5 to 1.3 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.030 |
Silicon (Si), % | 0 | |
0 to 0.5 |
Sulfur (S), % | 0.080 to 0.13 | |
0 to 0.0050 |
Tungsten (W), % | 0 | |
0.25 to 1.3 |