SAE-AISI 1132 Steel vs. EN 1.5682 Steel
Both SAE-AISI 1132 steel and EN 1.5682 steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1132 steel and the bottom bar is EN 1.5682 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 210 | |
| 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 18 | |
| 21 |
| Fatigue Strength, MPa | 240 to 380 | |
| 400 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 72 |
| Shear Strength, MPa | 400 to 440 | |
| 480 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 720 | |
| 770 |
| Tensile Strength: Yield (Proof), MPa | 350 to 590 | |
| 570 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 430 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 8.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 9.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 7.5 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.3 |
| Embodied Energy, MJ/kg | 19 | |
| 31 |
| Embodied Water, L/kg | 48 | |
| 63 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 93 to 97 | |
| 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 940 | |
| 870 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 25 | |
| 27 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 23 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 23 |
Alloy Composition
| Carbon (C), % | 0.24 to 0.34 | |
| 0 to 0.13 |
| Copper (Cu), % | 0 | |
| 0 to 0.3 |
| Iron (Fe), % | 97.8 to 98.3 | |
| 88.7 to 91.1 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0.3 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 8.5 to 9.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 to 0.0050 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |