SAE-AISI 1132 Steel vs. S30601 Stainless Steel
Both SAE-AISI 1132 steel and S30601 stainless steel are iron alloys. They have 59% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1132 steel and the bottom bar is S30601 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 210 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 18 | |
| 37 |
| Fatigue Strength, MPa | 240 to 380 | |
| 250 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Reduction in Area, % | 39 to 46 | |
| 56 |
| Shear Modulus, GPa | 73 | |
| 75 |
| Shear Strength, MPa | 400 to 440 | |
| 450 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 720 | |
| 660 |
| Tensile Strength: Yield (Proof), MPa | 350 to 590 | |
| 300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 950 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1360 |
| Melting Onset (Solidus), °C | 1420 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 500 |
| Thermal Expansion, µm/m-K | 13 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 20 |
| Density, g/cm3 | 7.8 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.9 |
| Embodied Energy, MJ/kg | 19 | |
| 55 |
| Embodied Water, L/kg | 48 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 93 to 97 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 to 940 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 25 | |
| 24 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 22 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.24 to 0.34 | |
| 0 to 0.015 |
| Chromium (Cr), % | 0 | |
| 17 to 18 |
| Copper (Cu), % | 0 | |
| 0 to 0.35 |
| Iron (Fe), % | 97.8 to 98.3 | |
| 56.9 to 60.5 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 17 to 18 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 5.0 to 5.6 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 to 0.013 |