SAE-AISI 1141 Steel vs. ASTM Grade HG10 MNN Steel

Both SAE-AISI 1141 steel and ASTM grade HG10 MNN steel are iron alloys. They have 64% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1141 steel and the bottom bar is ASTM grade HG10 MNN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
170
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 17
23
Fatigue Strength, MPa 270 to 430
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Tensile Strength: Ultimate (UTS), MPa 740 to 810
590
Tensile Strength: Yield (Proof), MPa 400 to 700
250

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
990
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 12
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
21
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
4.0
Embodied Energy, MJ/kg 19
58
Embodied Water, L/kg 47
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 86 to 110
110
Resilience: Unit (Modulus of Resilience), kJ/m3 430 to 1290
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 26 to 29
21
Strength to Weight: Bending, points 23 to 25
20
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 24 to 26
13

Alloy Composition

Carbon (C), % 0.37 to 0.45
0.070 to 0.11
Chromium (Cr), % 0
18.5 to 20.5
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 97.7 to 98.2
57.9 to 66.5
Manganese (Mn), % 1.4 to 1.7
3.0 to 5.0
Molybdenum (Mo), % 0
0.25 to 0.45
Nickel (Ni), % 0
11.5 to 13.5
Niobium (Nb), % 0
0.2 to 1.0
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0
0 to 0.7
Sulfur (S), % 0.080 to 0.13
0 to 0.030