SAE-AISI 1141 Steel vs. Solder Alloy 601
SAE-AISI 1141 steel belongs to the iron alloys classification, while solder alloy 601 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1141 steel and the bottom bar is solder alloy 601.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 220 | |
| 5.0 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 31 |
| Elongation at Break, % | 11 to 17 | |
| 83 |
| Poisson's Ratio | 0.29 | |
| 0.41 |
| Shear Modulus, GPa | 72 | |
| 11 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 810 | |
| 12 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 43 |
| Melting Completion (Liquidus), °C | 1460 | |
| 120 |
| Melting Onset (Solidus), °C | 1420 | |
| 120 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 230 |
| Thermal Conductivity, W/m-K | 51 | |
| 34 |
| Thermal Expansion, µm/m-K | 12 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 12 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 14 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 7.3 |
| Embodied Water, L/kg | 47 | |
| 1330 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 2.3 |
| Stiffness to Weight: Bending, points | 24 | |
| 14 |
| Strength to Weight: Axial, points | 26 to 29 | |
| 0.45 |
| Strength to Weight: Bending, points | 23 to 25 | |
| 1.6 |
| Thermal Diffusivity, mm2/s | 14 | |
| 20 |
| Thermal Shock Resistance, points | 24 to 26 | |
| 1.2 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.1 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0.37 to 0.45 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.050 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 51 to 52.5 |
| Iron (Fe), % | 97.7 to 98.2 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 |
| Tin (Sn), % | 0 | |
| 47.5 to 48.5 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |