SAE-AISI 1141 Steel vs. SAE-AISI H43 Steel
Both SAE-AISI 1141 steel and SAE-AISI H43 steel are iron alloys. They have 85% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1141 steel and the bottom bar is SAE-AISI H43 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 72 | |
77 |
Tensile Strength: Ultimate (UTS), MPa | 740 to 810 | |
710 to 2140 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
270 |
Melting Completion (Liquidus), °C | 1460 | |
1530 |
Melting Onset (Solidus), °C | 1420 | |
1480 |
Specific Heat Capacity, J/kg-K | 470 | |
460 |
Thermal Conductivity, W/m-K | 51 | |
30 |
Thermal Expansion, µm/m-K | 12 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.9 | |
14 |
Density, g/cm3 | 7.8 | |
7.9 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
8.2 |
Embodied Energy, MJ/kg | 19 | |
120 |
Embodied Water, L/kg | 47 | |
100 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 26 to 29 | |
25 to 75 |
Strength to Weight: Bending, points | 23 to 25 | |
22 to 46 |
Thermal Diffusivity, mm2/s | 14 | |
8.3 |
Thermal Shock Resistance, points | 24 to 26 | |
21 to 62 |
Alloy Composition
Carbon (C), % | 0.37 to 0.45 | |
0.5 to 0.65 |
Chromium (Cr), % | 0 | |
3.8 to 4.5 |
Iron (Fe), % | 97.7 to 98.2 | |
83.2 to 85.9 |
Manganese (Mn), % | 1.4 to 1.7 | |
0.15 to 0.4 |
Molybdenum (Mo), % | 0 | |
7.8 to 8.5 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.030 |
Silicon (Si), % | 0 | |
0.2 to 0.45 |
Sulfur (S), % | 0.080 to 0.13 | |
0 to 0.030 |
Vanadium (V), % | 0 | |
1.8 to 2.2 |