SAE-AISI 1141 Steel vs. C77600 Nickel Silver
SAE-AISI 1141 steel belongs to the iron alloys classification, while C77600 nickel silver belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1141 steel and the bottom bar is C77600 nickel silver.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 11 to 17 | |
| 30 |
| Poisson's Ratio | 0.29 | |
| 0.3 |
| Shear Modulus, GPa | 72 | |
| 43 |
| Shear Strength, MPa | 460 to 480 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 740 to 810 | |
| 630 |
| Tensile Strength: Yield (Proof), MPa | 400 to 700 | |
| 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 140 |
| Melting Completion (Liquidus), °C | 1460 | |
| 830 |
| Melting Onset (Solidus), °C | 1420 | |
| 790 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 31 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 27 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.7 |
| Embodied Energy, MJ/kg | 19 | |
| 60 |
| Embodied Water, L/kg | 47 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 110 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 430 to 1290 | |
| 470 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.9 |
| Stiffness to Weight: Bending, points | 24 | |
| 20 |
| Strength to Weight: Axial, points | 26 to 29 | |
| 22 |
| Strength to Weight: Bending, points | 23 to 25 | |
| 21 |
| Thermal Shock Resistance, points | 24 to 26 | |
| 20 |
Alloy Composition
| Carbon (C), % | 0.37 to 0.45 | |
| 0 |
| Copper (Cu), % | 0 | |
| 42 to 45 |
| Iron (Fe), % | 97.7 to 98.2 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 | |
| 0 to 0.25 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0 to 0.25 |
| Nickel (Ni), % | 0 | |
| 12 to 14 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 | |
| 39.7 to 46 |
| Residuals, % | 0 | |
| 0 to 0.5 |