SAE-AISI 1144 Steel vs. EN 1.5638 Steel

Both SAE-AISI 1144 steel and EN 1.5638 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1144 steel and the bottom bar is EN 1.5638 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220 to 230
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 17
23
Fatigue Strength, MPa 280 to 430
290
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 750 to 840
580
Tensile Strength: Yield (Proof), MPa 420 to 690
410

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
4.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.7
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 47
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91 to 110
120
Resilience: Unit (Modulus of Resilience), kJ/m3 480 to 1290
450
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 27 to 30
20
Strength to Weight: Bending, points 23 to 25
20
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 22 to 24
17

Alloy Composition

Carbon (C), % 0.4 to 0.48
0.060 to 0.12
Iron (Fe), % 97.5 to 98
94.4 to 96.4
Manganese (Mn), % 1.4 to 1.7
0.5 to 0.8
Nickel (Ni), % 0
3.0 to 4.0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0.24 to 0.33
0 to 0.015