SAE-AISI 1146 Steel vs. C99500 Copper
SAE-AISI 1146 steel belongs to the iron alloys classification, while C99500 copper belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1146 steel and the bottom bar is C99500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 13 to 17 | |
| 13 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 45 |
| Tensile Strength: Ultimate (UTS), MPa | 670 to 730 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 360 to 630 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 210 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1090 |
| Melting Onset (Solidus), °C | 1420 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 30 |
| Density, g/cm3 | 7.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.0 |
| Embodied Energy, MJ/kg | 18 | |
| 47 |
| Embodied Water, L/kg | 46 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 93 to 97 | |
| 63 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 340 to 1050 | |
| 410 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.7 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 24 to 26 | |
| 17 |
| Strength to Weight: Bending, points | 22 to 23 | |
| 17 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.5 to 2.0 |
| Carbon (C), % | 0.42 to 0.49 | |
| 0 |
| Copper (Cu), % | 0 | |
| 82.5 to 92 |
| Iron (Fe), % | 98.3 to 98.8 | |
| 3.0 to 5.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.25 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 3.5 to 5.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0.5 to 2.0 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0.5 to 2.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |