SAE-AISI 1151 Steel vs. S30530 Stainless Steel
Both SAE-AISI 1151 steel and S30530 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1151 steel and the bottom bar is S30530 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 210 to 220 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 11 to 17 | |
| 46 |
| Fatigue Strength, MPa | 260 to 410 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 72 | |
| 77 |
| Shear Strength, MPa | 430 to 480 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 710 to 800 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 390 to 660 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 970 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1410 |
| Melting Onset (Solidus), °C | 1420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 51 | |
| 15 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 2.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 12 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 18 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 3.4 |
| Embodied Energy, MJ/kg | 18 | |
| 48 |
| Embodied Water, L/kg | 46 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 86 to 100 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 1170 | |
| 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 21 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 4.1 |
| Thermal Shock Resistance, points | 22 to 25 | |
| 13 |
Alloy Composition
| Carbon (C), % | 0.48 to 0.55 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 17 to 20.5 |
| Copper (Cu), % | 0 | |
| 0.75 to 3.5 |
| Iron (Fe), % | 98.3 to 98.7 | |
| 58.4 to 72.5 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0.75 to 1.5 |
| Nickel (Ni), % | 0 | |
| 8.5 to 11.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 | |
| 0.5 to 2.5 |
| Sulfur (S), % | 0.080 to 0.13 | |
| 0 to 0.030 |