SAE-AISI 1212 Steel vs. SAE-AISI 1541 Steel
Both SAE-AISI 1212 steel and SAE-AISI 1541 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is SAE-AISI 1212 steel and the bottom bar is SAE-AISI 1541 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 180 | |
| 210 to 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 28 | |
| 11 to 17 |
| Fatigue Strength, MPa | 200 to 290 | |
| 260 to 420 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 39 to 51 | |
| 34 to 51 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 280 to 370 | |
| 440 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 620 | |
| 720 to 790 |
| Tensile Strength: Yield (Proof), MPa | 260 to 460 | |
| 390 to 680 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 52 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 to 110 | |
| 78 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 560 | |
| 410 to 1250 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 22 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 23 to 24 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 14 to 20 | |
| 23 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.13 | |
| 0.36 to 0.44 |
| Iron (Fe), % | 98.5 to 99.07 | |
| 97.8 to 98.3 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 1.4 to 1.7 |
| Phosphorus (P), % | 0.070 to 0.12 | |
| 0 to 0.040 |
| Sulfur (S), % | 0.16 to 0.23 | |
| 0 to 0.050 |