SAE-AISI 1213 Steel vs. EN 1.4630 Stainless Steel

Both SAE-AISI 1213 steel and EN 1.4630 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1213 steel and the bottom bar is EN 1.4630 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 11 to 29
23
Fatigue Strength, MPa 200 to 290
170
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 290 to 360
300
Tensile Strength: Ultimate (UTS), MPa 440 to 600
480
Tensile Strength: Yield (Proof), MPa 260 to 470
250

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
800
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
28
Thermal Expansion, µm/m-K 12
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
9.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.5
Embodied Energy, MJ/kg 18
36
Embodied Water, L/kg 46
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63 to 110
92
Resilience: Unit (Modulus of Resilience), kJ/m3 180 to 580
160
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 16 to 21
17
Strength to Weight: Bending, points 17 to 20
18
Thermal Diffusivity, mm2/s 14
7.5
Thermal Shock Resistance, points 14 to 19
17

Alloy Composition

Aluminum (Al), % 0
0 to 1.5
Carbon (C), % 0 to 0.13
0 to 0.030
Chromium (Cr), % 0
13 to 16
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 98.4 to 99
77.1 to 86.7
Manganese (Mn), % 0.7 to 1.0
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.5
Phosphorus (P), % 0.070 to 0.12
0 to 0.050
Silicon (Si), % 0
0.2 to 1.5
Sulfur (S), % 0.24 to 0.33
0 to 0.050
Titanium (Ti), % 0
0.15 to 0.8