SAE-AISI 1213 Steel vs. SAE-AISI 1330 Steel
Both SAE-AISI 1213 steel and SAE-AISI 1330 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1213 steel and the bottom bar is SAE-AISI 1330 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 190 | |
| 150 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 29 | |
| 11 to 23 |
| Fatigue Strength, MPa | 200 to 290 | |
| 210 to 380 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 290 to 360 | |
| 330 to 430 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 600 | |
| 520 to 710 |
| Tensile Strength: Yield (Proof), MPa | 260 to 470 | |
| 290 to 610 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 to 110 | |
| 76 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 580 | |
| 230 to 990 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 21 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 17 to 20 | |
| 18 to 23 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 17 to 23 |
Alloy Composition
| Carbon (C), % | 0 to 0.13 | |
| 0.28 to 0.33 |
| Iron (Fe), % | 98.4 to 99 | |
| 97.3 to 98 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 1.6 to 1.9 |
| Phosphorus (P), % | 0.070 to 0.12 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0.24 to 0.33 | |
| 0 to 0.040 |