SAE-AISI 1213 Steel vs. N08221 Nickel
SAE-AISI 1213 steel belongs to the iron alloys classification, while N08221 nickel belongs to the nickel alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1213 steel and the bottom bar is N08221 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 11 to 29 | |
| 34 |
| Fatigue Strength, MPa | 200 to 290 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Shear Strength, MPa | 290 to 360 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 600 | |
| 610 |
| Tensile Strength: Yield (Proof), MPa | 260 to 470 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 980 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1440 |
| Melting Onset (Solidus), °C | 1420 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 44 |
| Density, g/cm3 | 7.8 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 7.9 |
| Embodied Energy, MJ/kg | 18 | |
| 110 |
| Embodied Water, L/kg | 46 | |
| 240 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 to 110 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 580 | |
| 170 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 21 | |
| 21 |
| Strength to Weight: Bending, points | 17 to 20 | |
| 19 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.2 |
| Carbon (C), % | 0 to 0.13 | |
| 0 to 0.025 |
| Chromium (Cr), % | 0 | |
| 20 to 22 |
| Copper (Cu), % | 0 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 98.4 to 99 | |
| 22 to 33.9 |
| Manganese (Mn), % | 0.7 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 5.0 to 6.5 |
| Nickel (Ni), % | 0 | |
| 39 to 46 |
| Phosphorus (P), % | 0.070 to 0.12 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Sulfur (S), % | 0.24 to 0.33 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.6 to 1.0 |