SAE-AISI 12L14 Steel vs. ASTM A387 Grade 11 Steel
Both SAE-AISI 12L14 steel and ASTM A387 grade 11 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 12L14 steel and the bottom bar is ASTM A387 grade 11 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 170 | |
| 150 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 25 | |
| 25 |
| Fatigue Strength, MPa | 190 to 290 | |
| 200 to 250 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 280 to 370 | |
| 320 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 620 | |
| 500 to 600 |
| Tensile Strength: Yield (Proof), MPa | 260 to 460 | |
| 270 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 430 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 39 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 2.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.6 |
| Embodied Energy, MJ/kg | 18 | |
| 21 |
| Embodied Water, L/kg | 47 | |
| 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 to 93 | |
| 100 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 560 | |
| 200 to 320 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 22 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 14 | |
| 11 |
| Thermal Shock Resistance, points | 14 to 20 | |
| 15 to 18 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0.050 to 0.17 |
| Chromium (Cr), % | 0 | |
| 1.0 to 1.5 |
| Iron (Fe), % | 97.9 to 98.7 | |
| 96.2 to 97.6 |
| Lead (Pb), % | 0.15 to 0.35 | |
| 0 |
| Manganese (Mn), % | 0.85 to 1.2 | |
| 0.4 to 0.65 |
| Molybdenum (Mo), % | 0 | |
| 0.45 to 0.65 |
| Phosphorus (P), % | 0.040 to 0.090 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0.5 to 0.8 |
| Sulfur (S), % | 0.26 to 0.35 | |
| 0 to 0.025 |