SAE-AISI 12L14 Steel vs. C19500 Copper
SAE-AISI 12L14 steel belongs to the iron alloys classification, while C19500 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 12L14 steel and the bottom bar is C19500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 11 to 25 | |
| 2.3 to 38 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 72 | |
| 44 |
| Shear Strength, MPa | 280 to 370 | |
| 260 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 620 | |
| 380 to 640 |
| Tensile Strength: Yield (Proof), MPa | 260 to 460 | |
| 120 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1090 |
| Melting Onset (Solidus), °C | 1420 | |
| 1090 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 51 | |
| 200 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 50 to 56 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 50 to 57 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 31 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 18 | |
| 42 |
| Embodied Water, L/kg | 47 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 to 93 | |
| 14 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 560 | |
| 59 to 1530 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 22 | |
| 12 to 20 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 13 to 18 |
| Thermal Diffusivity, mm2/s | 14 | |
| 58 |
| Thermal Shock Resistance, points | 14 to 20 | |
| 13 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.020 |
| Carbon (C), % | 0 to 0.15 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 0.3 to 1.3 |
| Copper (Cu), % | 0 | |
| 94.9 to 98.6 |
| Iron (Fe), % | 97.9 to 98.7 | |
| 1.0 to 2.0 |
| Lead (Pb), % | 0.15 to 0.35 | |
| 0 to 0.020 |
| Manganese (Mn), % | 0.85 to 1.2 | |
| 0 |
| Phosphorus (P), % | 0.040 to 0.090 | |
| 0.010 to 0.35 |
| Sulfur (S), % | 0.26 to 0.35 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.1 to 1.0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.2 |