SAE-AISI 12L14 Steel vs. N07041 Nickel
SAE-AISI 12L14 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 12L14 steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 11 to 25 | |
| 14 |
| Fatigue Strength, MPa | 190 to 290 | |
| 540 |
| Shear Strength, MPa | 280 to 370 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 440 to 620 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 260 to 460 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1420 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 51 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 64 to 93 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 to 560 | |
| 2510 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 15 to 22 | |
| 47 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 34 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.0 |
| Thermal Shock Resistance, points | 14 to 20 | |
| 38 |