SAE-AISI 1345 Steel vs. EN 1.4369 Stainless Steel

Both SAE-AISI 1345 steel and EN 1.4369 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1345 steel and the bottom bar is EN 1.4369 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 170 to 210
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 23
40
Fatigue Strength, MPa 230 to 390
330
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Shear Strength, MPa 370 to 440
580
Tensile Strength: Ultimate (UTS), MPa 590 to 730
850
Tensile Strength: Yield (Proof), MPa 330 to 620
390

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
940
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
14
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 48
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78 to 120
280
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 1040
380
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21 to 26
31
Strength to Weight: Bending, points 20 to 23
26
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 19 to 23
18

Alloy Composition

Carbon (C), % 0.43 to 0.48
0.070 to 0.15
Chromium (Cr), % 0
17.5 to 19.5
Iron (Fe), % 97.2 to 97.8
63 to 70.2
Manganese (Mn), % 1.6 to 1.9
5.0 to 7.5
Nickel (Ni), % 0
6.5 to 8.5
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0.5 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015