SAE-AISI 1345 Steel vs. SAE-AISI 1524 Steel
Both SAE-AISI 1345 steel and SAE-AISI 1524 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1345 steel and the bottom bar is SAE-AISI 1524 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 210 | |
| 170 to 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 11 to 23 | |
| 14 to 22 |
| Fatigue Strength, MPa | 230 to 390 | |
| 230 to 340 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 370 to 440 | |
| 360 to 390 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 730 | |
| 570 to 650 |
| Tensile Strength: Yield (Proof), MPa | 330 to 620 | |
| 320 to 540 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 52 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 8.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 9.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 48 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 120 | |
| 84 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 1040 | |
| 270 to 760 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 to 26 | |
| 20 to 23 |
| Strength to Weight: Bending, points | 20 to 23 | |
| 19 to 21 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 19 to 23 | |
| 18 to 21 |
Alloy Composition
| Carbon (C), % | 0.43 to 0.48 | |
| 0.19 to 0.25 |
| Iron (Fe), % | 97.2 to 97.8 | |
| 98 to 98.5 |
| Manganese (Mn), % | 1.6 to 1.9 | |
| 1.4 to 1.7 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.050 |