SAE-AISI 1345 Steel vs. C16200 Copper

SAE-AISI 1345 steel belongs to the iron alloys classification, while C16200 copper belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1345 steel and the bottom bar is C16200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 11 to 23
2.0 to 56
Fatigue Strength, MPa 230 to 390
100 to 210
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 72
43
Shear Strength, MPa 370 to 440
190 to 390
Tensile Strength: Ultimate (UTS), MPa 590 to 730
240 to 550
Tensile Strength: Yield (Proof), MPa 330 to 620
48 to 470

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 400
370
Melting Completion (Liquidus), °C 1450
1080
Melting Onset (Solidus), °C 1410
1030
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 51
360
Thermal Expansion, µm/m-K 12
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
90
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
90

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
30
Density, g/cm3 7.8
9.0
Embodied Carbon, kg CO2/kg material 1.4
2.6
Embodied Energy, MJ/kg 19
41
Embodied Water, L/kg 48
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78 to 120
10 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 1040
10 to 970
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 21 to 26
7.4 to 17
Strength to Weight: Bending, points 20 to 23
9.6 to 17
Thermal Diffusivity, mm2/s 14
100
Thermal Shock Resistance, points 19 to 23
8.7 to 20

Alloy Composition

Cadmium (Cd), % 0
0.7 to 1.2
Carbon (C), % 0.43 to 0.48
0
Copper (Cu), % 0
98.6 to 99.3
Iron (Fe), % 97.2 to 97.8
0 to 0.2
Manganese (Mn), % 1.6 to 1.9
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0.15 to 0.35
0
Sulfur (S), % 0 to 0.040
0