SAE-AISI 1524 Steel vs. SAE-AISI 4130 Steel
Both SAE-AISI 1524 steel and SAE-AISI 4130 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1524 steel and the bottom bar is SAE-AISI 4130 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 170 to 180 | |
| 200 to 300 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 22 | |
| 13 to 26 |
| Fatigue Strength, MPa | 230 to 340 | |
| 320 to 660 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 360 to 390 | |
| 340 to 640 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 650 | |
| 530 to 1040 |
| Tensile Strength: Yield (Proof), MPa | 320 to 540 | |
| 440 to 980 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 420 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 43 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.3 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.5 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 19 | |
| 20 |
| Embodied Water, L/kg | 48 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 84 to 110 | |
| 83 to 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 760 | |
| 500 to 2550 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 20 to 23 | |
| 19 to 37 |
| Strength to Weight: Bending, points | 19 to 21 | |
| 19 to 29 |
| Thermal Diffusivity, mm2/s | 14 | |
| 12 |
| Thermal Shock Resistance, points | 18 to 21 | |
| 16 to 31 |
Alloy Composition
| Carbon (C), % | 0.19 to 0.25 | |
| 0.28 to 0.33 |
| Chromium (Cr), % | 0 | |
| 0.8 to 1.1 |
| Iron (Fe), % | 98 to 98.5 | |
| 97.3 to 98.2 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0.4 to 0.6 |
| Molybdenum (Mo), % | 0 | |
| 0.15 to 0.25 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 to 0.040 |