SAE-AISI 1541 Steel vs. CR016A Copper
SAE-AISI 1541 steel belongs to the iron alloys classification, while CR016A copper belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 1541 steel and the bottom bar is CR016A copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 11 to 17 | |
| 15 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 720 to 790 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 390 to 680 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1090 |
| Melting Onset (Solidus), °C | 1420 | |
| 1040 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 52 | |
| 390 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 98 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 99 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 35 |
| Density, g/cm3 | 7.8 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 19 | |
| 42 |
| Embodied Water, L/kg | 48 | |
| 390 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 78 to 100 | |
| 31 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 410 to 1250 | |
| 83 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 25 to 28 | |
| 7.1 |
| Strength to Weight: Bending, points | 23 to 24 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 14 | |
| 110 |
| Thermal Shock Resistance, points | 23 to 25 | |
| 8.1 |
Alloy Composition
| Bismuth (Bi), % | 0 | |
| 0 to 0.00050 |
| Carbon (C), % | 0.36 to 0.44 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.843 to 99.919 |
| Iron (Fe), % | 97.8 to 98.3 | |
| 0 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0.0010 to 0.0070 |
| Silver (Ag), % | 0 | |
| 0.080 to 0.12 |
| Sulfur (S), % | 0 to 0.050 | |
| 0 |