SAE-AISI 1541 Steel vs. N08330 Stainless Steel

Both SAE-AISI 1541 steel and N08330 stainless steel are iron alloys. They have 44% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1541 steel and the bottom bar is N08330 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 220
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 11 to 17
34
Fatigue Strength, MPa 260 to 420
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 440 to 480
360
Tensile Strength: Ultimate (UTS), MPa 720 to 790
550
Tensile Strength: Yield (Proof), MPa 390 to 680
230

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1050
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1340
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 52
12
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
32
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
5.4
Embodied Energy, MJ/kg 19
77
Embodied Water, L/kg 48
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 78 to 100
150
Resilience: Unit (Modulus of Resilience), kJ/m3 410 to 1250
140
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
19
Strength to Weight: Bending, points 23 to 24
18
Thermal Diffusivity, mm2/s 14
3.1
Thermal Shock Resistance, points 23 to 25
13

Alloy Composition

Carbon (C), % 0.36 to 0.44
0 to 0.080
Chromium (Cr), % 0
17 to 20
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 97.8 to 98.3
38.3 to 48.3
Lead (Pb), % 0
0 to 0.0050
Manganese (Mn), % 1.4 to 1.7
0 to 2.0
Nickel (Ni), % 0
34 to 37
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0
0.75 to 1.5
Sulfur (S), % 0 to 0.050
0 to 0.030
Tin (Sn), % 0
0 to 0.025