SAE-AISI 1547 Steel vs. C51000 Bronze

SAE-AISI 1547 steel belongs to the iron alloys classification, while C51000 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1547 steel and the bottom bar is C51000 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 11 to 17
2.7 to 64
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
42
Shear Strength, MPa 440 to 480
250 to 460
Tensile Strength: Ultimate (UTS), MPa 740 to 800
330 to 780
Tensile Strength: Yield (Proof), MPa 400 to 690
130 to 750

Thermal Properties

Latent Heat of Fusion, J/g 250
200
Maximum Temperature: Mechanical, °C 400
190
Melting Completion (Liquidus), °C 1460
1050
Melting Onset (Solidus), °C 1420
960
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 51
77
Thermal Expansion, µm/m-K 12
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
18
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
18

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
33
Density, g/cm3 7.8
8.8
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 19
50
Embodied Water, L/kg 47
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 80 to 110
7.0 to 490
Resilience: Unit (Modulus of Resilience), kJ/m3 430 to 1280
75 to 2490
Stiffness to Weight: Axial, points 13
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 26 to 28
10 to 25
Strength to Weight: Bending, points 23 to 24
12 to 21
Thermal Diffusivity, mm2/s 14
23
Thermal Shock Resistance, points 23 to 25
12 to 28

Alloy Composition

Carbon (C), % 0.43 to 0.51
0
Copper (Cu), % 0
92.9 to 95.5
Iron (Fe), % 97.8 to 98.2
0 to 0.1
Lead (Pb), % 0
0 to 0.050
Manganese (Mn), % 1.4 to 1.7
0
Phosphorus (P), % 0 to 0.040
0.030 to 0.35
Sulfur (S), % 0 to 0.050
0
Tin (Sn), % 0
4.5 to 5.8
Zinc (Zn), % 0
0 to 0.3
Residuals, % 0
0 to 0.5