SAE-AISI 4023 Steel vs. EN 1.1132 Steel

Both SAE-AISI 4023 steel and EN 1.1132 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4023 steel and the bottom bar is EN 1.1132 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
12 to 24
Fatigue Strength, MPa 170
180 to 280
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 280
260 to 310
Tensile Strength: Ultimate (UTS), MPa 440
370 to 490
Tensile Strength: Yield (Proof), MPa 230
240 to 400

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 47
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 86
38 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
160 to 430
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
13 to 17
Strength to Weight: Bending, points 16
15 to 18
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 14
12 to 16

Alloy Composition

Carbon (C), % 0.2 to 0.25
0.13 to 0.17
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 98.1 to 98.8
98.6 to 99.57
Manganese (Mn), % 0.7 to 0.9
0.3 to 0.6
Molybdenum (Mo), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0.15 to 0.35
0 to 0.3
Sulfur (S), % 0 to 0.040
0 to 0.025