SAE-AISI 4028 Steel vs. SAE-AISI S2 Steel

Both SAE-AISI 4028 steel and SAE-AISI S2 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4028 steel and the bottom bar is SAE-AISI S2 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Tensile Strength: Ultimate (UTS), MPa 490 to 630
670 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
44
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
2.1
Embodied Energy, MJ/kg 19
30
Embodied Water, L/kg 47
49

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17 to 22
24 to 69
Strength to Weight: Bending, points 18 to 21
22 to 44
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 16 to 20
23 to 68

Alloy Composition

Carbon (C), % 0.25 to 0.3
0.4 to 0.55
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 98.1 to 98.7
96 to 98.1
Manganese (Mn), % 0.7 to 0.9
0.3 to 0.5
Molybdenum (Mo), % 0.2 to 0.3
0.3 to 0.6
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0.9 to 1.2
Sulfur (S), % 0.035 to 0.050
0 to 0.030
Vanadium (V), % 0
0 to 0.5

Comparable Variants