SAE-AISI 4140 Steel vs. Grade 36 Titanium
SAE-AISI 4140 steel belongs to the iron alloys classification, while grade 36 titanium belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 4140 steel and the bottom bar is grade 36 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 11 to 26 | |
| 11 |
| Fatigue Strength, MPa | 360 to 650 | |
| 300 |
| Poisson's Ratio | 0.29 | |
| 0.36 |
| Shear Modulus, GPa | 73 | |
| 39 |
| Shear Strength, MPa | 410 to 660 | |
| 320 |
| Tensile Strength: Ultimate (UTS), MPa | 690 to 1080 | |
| 530 |
| Tensile Strength: Yield (Proof), MPa | 590 to 990 | |
| 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 320 |
| Melting Completion (Liquidus), °C | 1460 | |
| 2020 |
| Melting Onset (Solidus), °C | 1420 | |
| 1950 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 420 |
| Thermal Expansion, µm/m-K | 13 | |
| 8.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 58 |
| Embodied Energy, MJ/kg | 20 | |
| 920 |
| Embodied Water, L/kg | 51 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 74 to 180 | |
| 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 920 to 2590 | |
| 1260 |
| Stiffness to Weight: Axial, points | 13 | |
| 9.3 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 25 to 38 | |
| 23 |
| Strength to Weight: Bending, points | 22 to 30 | |
| 23 |
| Thermal Shock Resistance, points | 20 to 32 | |
| 45 |
Alloy Composition
| Carbon (C), % | 0.38 to 0.43 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0.8 to 1.1 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0035 |
| Iron (Fe), % | 96.8 to 97.8 | |
| 0 to 0.030 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0 |
| Niobium (Nb), % | 0 | |
| 42 to 47 |
| Nitrogen (N), % | 0 | |
| 0 to 0.030 |
| Oxygen (O), % | 0 | |
| 0 to 0.16 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 52.3 to 58 |
| Residuals, % | 0 | |
| 0 to 0.4 |