SAE-AISI 4142 Steel vs. EN 2.4951 Nickel
SAE-AISI 4142 steel belongs to the iron alloys classification, while EN 2.4951 nickel belongs to the nickel alloys.
For each property being compared, the top bar is SAE-AISI 4142 steel and the bottom bar is EN 2.4951 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 | |
| 34 |
| Fatigue Strength, MPa | 250 | |
| 200 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 370 | |
| 500 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 750 |
| Tensile Strength: Yield (Proof), MPa | 370 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 1150 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1360 |
| Melting Onset (Solidus), °C | 1420 | |
| 1310 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 460 |
| Thermal Conductivity, W/m-K | 44 | |
| 12 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 1.6 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 1.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 60 |
| Density, g/cm3 | 7.8 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 9.3 |
| Embodied Energy, MJ/kg | 20 | |
| 130 |
| Embodied Water, L/kg | 51 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 200 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 190 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 21 | |
| 25 |
| Strength to Weight: Bending, points | 20 | |
| 22 |
| Thermal Diffusivity, mm2/s | 12 | |
| 3.1 |
| Thermal Shock Resistance, points | 19 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.3 |
| Carbon (C), % | 0.4 to 0.45 | |
| 0.080 to 0.15 |
| Chromium (Cr), % | 0.8 to 1.1 | |
| 18 to 21 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 96.8 to 97.8 | |
| 0 to 5.0 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 65.4 to 81.7 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.2 to 0.6 |