SAE-AISI 4142 Steel vs. N06060 Nickel

SAE-AISI 4142 steel belongs to the iron alloys classification, while N06060 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4142 steel and the bottom bar is N06060 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 20
45
Fatigue Strength, MPa 250
230
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
82
Shear Strength, MPa 370
490
Tensile Strength: Ultimate (UTS), MPa 590
700
Tensile Strength: Yield (Proof), MPa 370
270

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 420
980
Melting Completion (Liquidus), °C 1460
1510
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 470
430
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
65
Density, g/cm3 7.8
8.7
Embodied Carbon, kg CO2/kg material 1.5
12
Embodied Energy, MJ/kg 20
160
Embodied Water, L/kg 51
280

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
250
Resilience: Unit (Modulus of Resilience), kJ/m3 360
180
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21
22
Strength to Weight: Bending, points 20
20
Thermal Shock Resistance, points 19
19

Alloy Composition

Carbon (C), % 0.4 to 0.45
0 to 0.030
Chromium (Cr), % 0.8 to 1.1
19 to 22
Copper (Cu), % 0
0.25 to 1.3
Iron (Fe), % 96.8 to 97.8
0 to 14
Manganese (Mn), % 0.75 to 1.0
0 to 1.5
Molybdenum (Mo), % 0.15 to 0.25
12 to 14
Nickel (Ni), % 0
54 to 60
Niobium (Nb), % 0
0.5 to 1.3
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0.15 to 0.35
0 to 0.5
Sulfur (S), % 0 to 0.040
0 to 0.0050
Tungsten (W), % 0
0.25 to 1.3