SAE-AISI 4147 Steel vs. SAE-AISI 4024 Steel

Both SAE-AISI 4147 steel and SAE-AISI 4024 steel are iron alloys. They have a very high 99% of their average alloy composition in common.

For each property being compared, the top bar is SAE-AISI 4147 steel and the bottom bar is SAE-AISI 4024 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 20
14
Fatigue Strength, MPa 260
320
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 380
370
Tensile Strength: Ultimate (UTS), MPa 610
600
Tensile Strength: Yield (Proof), MPa 380
500

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 420
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 44
51
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5
Embodied Energy, MJ/kg 20
19
Embodied Water, L/kg 51
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
77
Resilience: Unit (Modulus of Resilience), kJ/m3 380
670
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 12
14
Thermal Shock Resistance, points 20
18

Alloy Composition

Carbon (C), % 0.45 to 0.5
0.2 to 0.25
Chromium (Cr), % 0.8 to 1.1
0
Iron (Fe), % 96.7 to 97.7
98.1 to 98.7
Manganese (Mn), % 0.75 to 1.0
0.7 to 0.9
Molybdenum (Mo), % 0.15 to 0.25
0.2 to 0.3
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0.15 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.040
0.035 to 0.050