SAE-AISI 4150 Steel vs. SAE-AISI 8655 Steel
Both SAE-AISI 4150 steel and SAE-AISI 8655 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is SAE-AISI 4150 steel and the bottom bar is SAE-AISI 8655 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 380 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 20 | |
| 23 |
| Fatigue Strength, MPa | 260 to 780 | |
| 290 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 410 to 800 | |
| 390 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 1310 | |
| 620 |
| Tensile Strength: Yield (Proof), MPa | 380 to 1220 | |
| 410 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 42 | |
| 39 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 2.6 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.5 |
| Embodied Energy, MJ/kg | 20 | |
| 20 |
| Embodied Water, L/kg | 51 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 82 to 180 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 380 to 3930 | |
| 440 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 47 | |
| 22 |
| Strength to Weight: Bending, points | 22 to 34 | |
| 21 |
| Thermal Diffusivity, mm2/s | 11 | |
| 10 |
| Thermal Shock Resistance, points | 19 to 39 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.48 to 0.53 | |
| 0.51 to 0.59 |
| Chromium (Cr), % | 0.8 to 1.1 | |
| 0.4 to 0.6 |
| Iron (Fe), % | 96.7 to 97.7 | |
| 96.4 to 97.6 |
| Manganese (Mn), % | 0.75 to 1.0 | |
| 0.75 to 1.0 |
| Molybdenum (Mo), % | 0.15 to 0.25 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 0 | |
| 0.4 to 0.7 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.035 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.040 |