SAE-AISI 4320 Steel vs. EN 1.7709 Steel
Both SAE-AISI 4320 steel and EN 1.7709 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is SAE-AISI 4320 steel and the bottom bar is EN 1.7709 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 160 to 240 | |
200 to 230 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
73 |
Tensile Strength: Ultimate (UTS), MPa | 570 to 790 | |
650 to 780 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 420 | |
440 |
Melting Completion (Liquidus), °C | 1460 | |
1470 |
Melting Onset (Solidus), °C | 1420 | |
1420 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 46 | |
33 |
Thermal Expansion, µm/m-K | 11 | |
11 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
7.5 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
8.6 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 3.4 | |
3.4 |
Density, g/cm3 | 7.9 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.7 | |
2.3 |
Embodied Energy, MJ/kg | 22 | |
32 |
Embodied Water, L/kg | 52 | |
56 |
Common Calculations
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 20 to 28 | |
23 to 27 |
Strength to Weight: Bending, points | 19 to 24 | |
21 to 24 |
Thermal Diffusivity, mm2/s | 13 | |
8.9 |
Thermal Shock Resistance, points | 19 to 27 | |
22 to 26 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.030 |
Carbon (C), % | 0.17 to 0.22 | |
0.17 to 0.25 |
Chromium (Cr), % | 0.4 to 0.6 | |
1.2 to 1.5 |
Iron (Fe), % | 95.8 to 97 | |
95.2 to 97.5 |
Manganese (Mn), % | 0.45 to 0.65 | |
0.4 to 0.8 |
Molybdenum (Mo), % | 0.2 to 0.3 | |
0.55 to 0.8 |
Nickel (Ni), % | 1.7 to 2.0 | |
0 to 0.6 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.025 |
Silicon (Si), % | 0.15 to 0.35 | |
0 to 0.4 |
Sulfur (S), % | 0 to 0.040 | |
0 to 0.030 |
Vanadium (V), % | 0 | |
0.2 to 0.35 |