SAE-AISI 4340 Steel vs. S45000 Stainless Steel

Both SAE-AISI 4340 steel and S45000 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 4340 steel and the bottom bar is S45000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210 to 360
280 to 410
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 12 to 22
6.8 to 14
Fatigue Strength, MPa 330 to 740
330 to 650
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
76
Shear Strength, MPa 430 to 770
590 to 830
Tensile Strength: Ultimate (UTS), MPa 690 to 1280
980 to 1410
Tensile Strength: Yield (Proof), MPa 470 to 1150
580 to 1310

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 430
840
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 44
17
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.6
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 3.5
13
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.7
2.8
Embodied Energy, MJ/kg 22
39
Embodied Water, L/kg 53
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 79 to 170
94 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 590 to 3490
850 to 4400
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24 to 45
35 to 50
Strength to Weight: Bending, points 22 to 33
28 to 36
Thermal Diffusivity, mm2/s 12
4.5
Thermal Shock Resistance, points 20 to 38
33 to 47

Alloy Composition

Carbon (C), % 0.38 to 0.43
0 to 0.050
Chromium (Cr), % 0.7 to 0.9
14 to 16
Copper (Cu), % 0
1.3 to 1.8
Iron (Fe), % 95.1 to 96.3
72.1 to 79.3
Manganese (Mn), % 0.6 to 0.8
0 to 1.0
Molybdenum (Mo), % 0.2 to 0.3
0.5 to 1.0
Nickel (Ni), % 1.7 to 2.0
5.0 to 7.0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0.15 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.030